點擊圖片查看大圖| 經(jīng)濟型NYLON 6 復(fù)合材料特性及應(yīng)用 | ||||||||||
| 經(jīng)濟型NYLON6復(fù)合材料 Economical Nylon 6 Composite | NYLON6加纖型(BR) Glass Fiber& Reinforced Bright | NYLON 6加纖型 (SD) Glass Fiber& Reinforced Semidull | ||||||||
| 物性Properties | 單位Unit | 品名Grade規(guī)范ASTM | N15G 153N1-K | N15G 203N1-K | N15G 303N1-K | N15G 453N1-K | N15G 303S1-E | N16G 453S2-E | N13G 503S1-N | |
| 抗張強度Tensile Strength | Kg/cm2 | D-638 | 900 | 950 | 1350 | 1600 | 1150 | 1400 | 1600 | |
| 抗張模數(shù)Tensile Modulus | Kg/cm2 | D-638 | ||||||||
| 伸長率Elongation | % | D-638 | 2.9 | 2.8 | 2.5 | 2.3 | 2.3 | 2 | 2 | |
| 抗折強度Flexural Strength | Kg/cm2 | D-790 | 1400 | 1600 | 2000 | 2400 | 1750 | 2100 | 2300 | |
| 抗折模數(shù)Flexural Modulus | Kg/cm2 | D-790 | 50000 | 60000 | 78000 | 110000 | 76500 | 110000 | 115000 | |
| 動擊強度Izod | kg-cm/cm | RT | D-256 | 5 | 6 | 11 | 14 | 7 | 10 | 13 |
| 硬度Hardness | Rockwell R | D-785 | 116 | 117 | 118 | 119 | 118 | 119 | 120 | |
| 熱變形溫度H D T | ℃ | 1.82Mpa | D-648 | 195 | 200 | 205 | 210 | 203 | 210 | 212 |
| 灰份Filler Content | % | D-2584 | 15 | 20 | 30 | 45 | 30 | 45 | 50 | |
| 比重Specific Gravity | D-792 | 1.22 | 1.27 | 1.34 | 1.5 | 1.35 | 1.5 | 1.55 | ||
| 模收縮率Mold Shrinkage | cm/cm | D-955 | 0.25-0.45 | 0.2-0.4 | 0.15-0.35 | 0.1-0.3 | 0.15-0.35 | 0.1-0.3 | 0.1-0.3 | |
| 特性:1.具高機械強度 | 成型條件: | |||||||||
| 2.耐韌及耐動擊性特優(yōu) | 1.干燥溫度時間100℃/3HRS | |||||||||
| 3.電氣特性佳 | 2.成型溫度:230-280℃ | |||||||||
| 4.耐化學(xué)藥品性佳 | 3.模具溫度:80-100℃ | |||||||||
| 5.耐磨擦性佳 | ||||||||||
| 備注:以上數(shù)值系參考ASTM試驗方法所測得,僅供選擇用途品級之參考. | ||||||||||