以下是PA6 Zytel 73G30HSL NC010中英文物性表
|
DuPont Zytel? 73G30HSL NC010 Nylon 6（聚酰胺-尼龍6）
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質(zhì)
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
Density密度
|
1.36 g/cc
|
0.0491 lb/in3
|
DAM; ISO 1183
|
|
Filler Content 填充的內(nèi)容
|
30 %
|
30 %
|
DAM
|
|
Water Absorption吸水率吸水率
|
1.9 %
@Temperature 23.0 °C |
1.9 %
@Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to
|
|
6.3 %
@Temperature 23.0 °C |
6.3 %
@Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to
|
|
|
Linear Mold Shrinkage, Flow線性收縮率/流動
|
0.0020 cm/cm
@Thickness 2.00 mm |
0.0020 in/in
@Thickness 0.0787 in |
Parallel; DAM; ISO 294-4
|
|
Linear Mold Shrinkage, Transverse線性收縮率/橫向
|
0.0060 cm/cm
@Thickness 2.00 mm |
0.0060 in/in
@Thickness 0.0787 in |
Normal; DAM; ISO 294-4
|
|
Melt Index of Compound熔體流動速率
|
4.0 g/10 min
@Load 2.16 kg, Temperature 250 °C |
4.0 g/10 min
@Load 4.76 lb, Temperature 482 °F |
DAM; cm3/10 min; ISO 1133
|
|
Mechanical Properties力學(xué)性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測試方法
|
|
Tensile Strength at Break斷裂拉伸強(qiáng)度
|
115 MPa
@Temperature 23.0 °C |
16700 psi
@Temperature 73.4 °F |
50%RH; ISO 527
|
|
185 MPa
@Temperature 23.0 °C |
26800 psi
@Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Elongation at Break斷裂伸長率
|
3.5 %
@Temperature 23.0 °C |
3.5 %
@Temperature 73.4 °F |
DAM; ISO 527
|
|
6.0 %
@Temperature 73.4 °F |
50%RH; ISO 527
|
||
|
Tensile Modulus拉伸模量
|
5.80 GPa
@Temperature 23.0 °C |
841 ksi
@Temperature 73.4 °F |
50%RH; ISO 527
|
|
9.70 GPa
@Temperature 23.0 °C |
1410 ksi
@Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度 (ISO)
|
10.0 kJ/m2
@Temperature -30.0 °C |
4.76 ft-lb/in2
@Temperature -22.0 °F |
DAM; ISO 180/1A
|
|
11.0 kJ/m2
@Temperature -30.0 °C |
5.23 ft-lb/in2
@Temperature -22.0 °F |
50%RH; ISO 180/1A
|
|
|
15.0 kJ/m2
@Temperature 23.0 °C |
7.14 ft-lb/in2
@Temperature 73.4 °F |
DAM; ISO 180/1A
|
|
|
20.0 kJ/m2
@Temperature 23.0 °C |
9.52 ft-lb/in2
@Temperature 73.4 °F |
50%RH; ISO 180/1A
|
|
|
Charpy Impact Unnotched夏比缺口試樣沖擊
|
8.00 J/cm2
@Temperature -30.0 °C |
38.1 ft-lb/in2
@Temperature -22.0 °F |
DAM; ISO 179/1eU
|
|
8.40 J/cm2
@Temperature -30.0 °C |
40.0 ft-lb/in2
@Temperature -22.0 °F |
50%RH; ISO 179/1eU
|
|