| NORYL PPX? Resin | ||
| Grades |
De |
|
| PPX630 |
30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). Datasheet Product Data: Engineering Design Data Auto Data: |
|
| PPX7110 |
PPE+PP blend. High Impact, Good Heat Resistance Datasheet Product Data: Engineering Design Data | Chemical Compatibility Auto Data: |
|
| PPX830 |
PPE+PP, 30% Glass reinforced, Low creep, HDT /1.8MPa of 153 deg C, Tensile modulus of 7600 MPa, UL-94 HB rated @ 1.00 mm, GWFI of 650 deg C @ 3.00 mm, Opaque, Limited colors available Datasheet Product Data: Auto Data: |
|
|
|
|||||||||||||||||||||||||||||||
| Compare | Contact Us | |
| NORYL GTX? Resin | ||
| Grades |
De |
|
| GTX626 |
Blowmolding and extrusion. High heat and chemical resistant. Datasheet Product Data: Engineering Design Data | Chemical Compatibility Auto Data: |
|
| GTX810 |
GR 10%. Increased stiffness of 200000 psi (3000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: lighting. Datasheet Product Data: Engineering Design Data | Chemical Compatibility Auto Data: Auto Specification |
|
| GTX830 |
GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. Datasheet Product Data: Engineering Design Data | Chemical Compatibility Auto Data: Auto Specification |
|
| GTX902 |
Unreinforced. Excellent chemical resistance and paintability. 312F (155C) HDT. Datasheet Product Data: Engineering Design Data | Chemical Compatibility Auto Data: Auto Specification |
|
| GTX910 |
Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance. Datasheet Product Data: Engineering Design Data | Chemical Compatibility Auto Data: Auto Specification |
|
| GTX918W |
High flow NORYL GTX resin for under-the-hood and electrical applications requiring retention of properties under thermal load Datasheet Product Data: Engineering Design Data | Chemical Compatibility Auto Data: Auto Specification |
|
| RNX130 |
30% glass reinforced PPE+PS+PA alloy for automotive and nonautomotive applications. Recycle grade in black/gray only. Datasheet Product Data: Auto Data: |
|
|
|
NORYL PPX ? Resin PPX830 |
SI | | British | | Metric | Americas: COMMERCIAL |
| NORYL PPX830 Polyphenylene Oxide (PPO?) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus of 7600 MPa; this grade has been developed for application where dimension stability, temperature and chemical resistance could be required. NORYL PPX830 is an opaque material available in limited colors only. |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 1020 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 1020 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2.9 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 101 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 77400 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1460 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 67300 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 98 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 98 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3.2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 7700 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 141 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 7100 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 66 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 9 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 152 | cm-kgf | ASTM D 3763 | |
| Instrumented Impact Total Energy, -30°C | 101 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m2 | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 42 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 39 | kJ/m2 | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 36 | kJ/m2 | ISO 179/1eU | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 166 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D 648 | |
| CTE, -40°C to 95°C, flow | 2.5E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 95°C, xflow | 1.3E-04 | 1/°C | ASTM E 831 | |
| CTE, -30°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, -30°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/120 | 150 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 168 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 153 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.19 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.2 - 0.25 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.4 - 0.6 | % | SABIC Method | |
| Melt Flow Rate, 280°C/5.0 kgf | 6 | g/10 min | ASTM D 1238 | |
| Density | 1.19 | g/cm3 | ISO 1183 | |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 6 | cm3/10 min | ISO 1133 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 1 | mm | UL 94 | |
| Glow Wire Flammability Index 650°C, passes at | 3 | mm | IEC 60695-2-12 | |
| Source GMD, last updated:2008/08/19 |
|
Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 65 - 75 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 300 | °C |
| Nozzle Temperature | 260 - 300 | °C |
| Front - Zone 3 Temperature | 255 - 290 | °C |
| Middle - Zone 2 Temperature | 250 - 290 | °C |
| Rear - Zone 1 Temperature | 245 - 290 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 40 - 65 | °C |
| Source GMD, last updated:2008/08/19 |
|
|