| SABIC Innovative Plastics LNP STAT-LOY A3000 ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer
|
||
| Material Notes: |
LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ISO 1183 |
| 1.065 g/cc | 0.03848 lb/in3 | ASTM D792 | |
| Moisture Absorption | 1.08 % | 1.08 % | 50% RH, 24 hrs; ASTM D570 |
Linear Mold Shrinkage, Flow 
|
0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
|
0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 | |
|
Linear Mold Shrinkage, Transverse
|
0.0049 cm/cm @Time 86400 sec |
0.0049 in/in @Time 24.0 hour |
ISO 294 |
|
0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ISO 527 |
| 36.0 MPa | 5220 psi | ASTM D638 | |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ISO 527 |
| 39.0 MPa | 5660 psi | ASTM D638 | |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| 24.2 % | 24.2 % | ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| 3.1 % | 3.1 % | ASTM D638 | |
| Tensile Modulus | 2.01 GPa | 292 ksi | 1 mm/min; ISO 527 |
| 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 59.0 MPa | 8560 psi | ISO 178 |
| 65.0 MPa | 9430 psi | ASTM D790 | |
| Flexural Modulus | 1.98 GPa | 287 ksi | ISO 178 |
| 2.09 GPa | 303 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.82 J/cm | 5.28 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m2 | 7.61 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 32.0 J | 23.6 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 26.0 J | 19.2 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
|
CTE, linear, Parallel to Flow
|
93.4 μm/m-°C @Temperature -40.0 - 40.0 °C |
51.9 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
93.4 μm/m-°C @Temperature -40.0 - 40.0 °C |
51.9 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
|
CTE, linear, Transverse to Flow
|
101 μm/m-°C @Temperature -40.0 - 40.0 °C |
56.1 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
101 μm/m-°C @Temperature -40.0 - 40.0 °C |
56.1 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 |
HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS
SABIC Innovative Plastics LNP STAT-LOY AF306 ABS
EMS-Grivory Grivory? 2D 25 W 20 HL X black 9992 PA612-I
DuPont Performance Polymers Crastin? FG6129 NC010 PBT
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。