| SABIC Innovative Plastics LNP STAT-LOY AF306 ABS | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer
|
||
| Material Notes: |
LNP* STAT-LOY* AF306 is a compound based on ABS resin containing 30% Glass Fiber. Added feature of this material is: Antistatic.
|
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in3 | ISO 1183 |
| 1.29 g/cc | 0.0466 lb/in3 | ASTM D792 | |
| Moisture Absorption | 3.00 % | 3.00 % | 50% RH, 24 hrs; ASTM D570 |
Linear Mold Shrinkage, Flow 
|
0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
|
0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ISO 294 | |
|
Linear Mold Shrinkage, Transverse
|
0.0045 cm/cm @Time 86400 sec |
0.0045 in/in @Time 24.0 hour |
ISO 294 |
|
0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| 43.0 MPa | 6240 psi | ISO 527 | |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ASTM D638 |
| 43.0 MPa | 6240 psi | ISO 527 | |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| 1.0 % | 1.0 % | ISO 527 | |
| Elongation at Yield | 1.0 % | 1.0 % | ASTM D638 |
| 1.1 % | 1.1 % | ISO 527 | |
| Tensile Modulus | 6.01 GPa | 872 ksi | 1 mm/min; ISO 527 |
| 6.89 GPa | 999 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| 63.0 MPa | 9140 psi | ISO 178 | |
| Flexural Modulus | 5.51 GPa | 799 ksi | ASTM D790 |
| 5.70 GPa | 827 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.50 J/cm | 4.68 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m2 | 8.09 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+6 - 1.00e+9 ohm | 1.00e+6 - 1.00e+9 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
|
CTE, linear, Parallel to Flow
|
113 μm/m-°C @Temperature -40.0 - 40.0 °C |
62.8 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
|
114 μm/m-°C @Temperature -40.0 - 40.0 °C |
63.3 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
|
CTE, linear, Transverse to Flow
|
43.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
|
43.2 μm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 μin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
SABIC Innovative Plastics LNP STAT-LOY AF306 ABS (Asia Pacific)
PTS Trilac? ABS-HS7500 High Impact ABS Resin
SABIC Innovative Plastics Cycolac? MG29 ABS
SABIC Innovative Plastics Cycolac? MG38 ABS
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。